UPM Communication Papers
Wish to be able to tailor your label release liner to suit your needs? It’s possible with these heavily calendered, transparent glassine papers. Glassines offer very good quality consistency, optimal surface properties, even thickness and strength.
Regions
South America | North America | Africa | Europe | Middle East
Business contact
Category
Base papers
Description
High quality release base paper with excellent surface properties for paper-based faces. Providing constant performance day-after-day. Yellow shade.
Grade
Glassine
End use
Label
Finish
Supercalendered
Converting method
UV cured silicone coating | Emulsion silicone coating | Solvent based silicone coating | Solventless silicone coating
Format/Size
Reels
Reel Diameter (cm)
80,0 - 135,0 / 147,0
Reel Width (cm)
50,0 - 230,0
Core (mm)
76,0 / 153,0
Wrapping
Strong kraft paper | Strong moisture proof polyethylene laminated kraft paper
Certificates and labels
ISO 22000 | FSC Chain-of-Custody | FDA Food Certificate | EN 71/3:1988 D Safety of Toys | 94/62 EC Heavy Metal Certificate | Food Approval Statement | BfR Food Certificate | PEFC Chain-of-Custody | EMAS | ISO 9001 | ISO 14001
Note
PEFC and FSC on request but subject to availability.
Technical target values (imperial in paranthesis)
Basis Weight (ISO 536) (g/m²) (lb/3000ft²)
56.0
(34.4)
57.0
(35.0)
58.0
(35.6)
60.0
(36.8)
Thickness (ISO 534) (µm) (mils)
49.0
(1.9)
50.0
(2.0)
51.0
(2.0)
53.0
(2.1)
Moisture (%)
6.5
6.5
6.5
6.5
Tensile Strength MD (kN/m) (lb/in)
6.0
(34.3)
6.2
(35.4)
6.4
(36.5)
6.6
(37.7)
Tensile Strength CD (kN/m) (lb/in)
2.3
(13.1)
2.4
(13.7)
2.5
(13.7)
2.5
(14.3)
Tear Strength MD (mN) (g)
290
(29.6)
300.0
(30.6)
305.0
(31.1)
325.0
(33.2)
Tear Strength CD (mN) (g)
310
(31.6)
315.0
(32.1)
320.0
(32.6)
340.0
(34.7)
Unger Oil Absorption (g/m²)
0.7
0.7
0.7
0.7
Transparency (%)
50
49.0
49.0
48.0
Roughness PPS10 TS (µm)
1.6
1.5
1.5
1.5
L-value C/2°
93
93.0
93.0
93.0
a-value C/2°
-1.0
-1.0
-1.0
-1.0
b-value C/2°
40.0
40.0
40.0
40.0
Porosity BEKK (s)
150.0
150.0
155.0
160.0
Imperial values indicated in paranthesis
Please note: Technical values are informative and subject to production variations.